Method for reducing iron oxides in a gaseous reduction process

ABSTRACT

This is a disclosure of a method and apparatus for reducing iron oxides to metallized pellets and includes the desulphurization of gases containing sulphur and/or compounds of sulphur, especially H2S. The disclosure is particularly concerned with the metallization of iron oxides through a gaseous reduction process wherein the spent gas is used to cool the pellets before discharge from the furnace, and then is upgraded for continued use. It has also been found that activated iron particles, such as sponge iron and metallized pellets, are highly effective for the removal of sulphur impurities from such gas.

United States Patent 1191 Beggs et a1.

1 1 June 11, 1974 [5 METHOD FOR REDUCING IRON OXIDES 3,199,946 8/1965 Fujita Ct a1 23/3 L IN A GASEOUS REDUCTION P O 3,375,098 3/1968 Marshall I Do Id Be T l d WW T 3,375,099 3/1968 Marshall 75/35 nventors: na ggs, e 0; 1 1am Marsh), whitehouse, both of Ohio FOREIGN PATENTS OR APPLICATIONS 4,279 01891 G B' ..233L [73] Assignee: Midrex Corporation, Toledo, Ohio rem mam [22] Fil d; D 10, 1969 Primary Examiner-L. Dewayne Rutledge Assistant Examiner--M. .1. Andrews [21] App! 8833 Attorney, Agent, or Firm-Peter Vrahotes; Henry Koz [52] US. Cl. 75/35 [51 1111.131 C2lb 13/02 ABSTRACT [58] Field of Search 75/35 This is a disclosure of a method and apparatus for reducing iron oxides to metallized pellets and includes [56] References Cited the desulphurization of gases containing sulphur and- UNITED STATES PATENTS /or compounds of sulphur, especially H S. The disclo- 1 800 856 4/1931 Bradley 75/35 sure is Particularly with metallizmio" of 1,871,848 8/1932 Gustafsson. 75/33 x iron Oxides through a gaseous reduction Process 2,528,553 11/1950 Royster 75/35 x wherein the Spent gas is used to @001 the Pellets before 2,545,932 3/ 1951 Tiddy ct a1 75/35 discharge from the furnace, and then is upgraded for 2.5 5.933 3/1951 Tiddy et al..-... 75/ continued use. It has also been found that activated 2,551,905 5/1951 Robinson 23/25 iron particles uch as sponge iron and metallized pe]- g 3L 1 lets, are highly effective for the removal of sulphur ime CI'S 2,931,720 4/1960 De Vaney 75/35 Pumas from Such 3,151,973 /1964 Halley 75/35 3 Claims, 1 Drawing Figure lZ Z4 Z6 3 a T Z5 \2; O l 92 I 9 u I 22 95 68 i j I Z I //'r I j I 7Z'\I '7 (i l I j I 40 73 1 3 J k ,C, i 5 f I, o 32 "1' METHOD FOR REDUCING IRON OXIDES IN A GASEOUS REDUCTION'IROCESS A need exists in many commercial processes for an effective and inexpensive method of removing sulphur and/or its compounds, particularly H S, from a process gas. One such process wherein this need exists is the reduction of iron oxide ores into metallized pellets wherein the iron oxide is reduced by a gas containing H and/or CO. Certain gaseous reduction processes utilize the spent gases, or offgases, by converting the H and CO, from such spent gases to H and CO through reaction of the off-gas with a hydrocarbon such as natural gas. When the iron ore contains a high percentage of sulphur, the sulphur reacts with the reducing gas to form H S which, of course, is a gas. The most widely used method of removing l-lgS from a gas is to utilize activated iron oxide chips in a bed. Although such a bed is effective in the removal of H S, the capital investment is large, and the size of the apparatus requires a considerable amount of space.

It is, therefore, an object of this invention to provide novel method and means for metallizing iron oxides.

It is another object of this invention to provide a novel method for removal of H 8 from a gas mixture.

lt is a furtherobject of this invention to provide a novel method for reducing iron oxide to metallic iron while removing sulphur from said iron oxide.

It is still another object to provide apparatus for metallizing iron oxide through a gaseous reduction means which includes sulphur removal means.

It is a still further object of this invention to provide method and means for a gaseous reduction process wherefull utilization of spent gases is achieved.

It has been found that activated iron particles are capable of effectively removing hydrogen sulphide from a reducing gas. Throughout this specification and the appended claims, the term activated iron particles is defined as that class of material resulting when iron ore or iron oxide is reacted with a reductant such as hydrogen, carbon monoxide,.solid carbonaceous material, or a hydrocarbon, and theiron oxide is converted to metallic iron by the reaction of the reductantwith the iron oxide to give off H Oand/or CO thereby leaving metallic iron in a highly reactive state. This includes sponge iron and metallized iron pellets.

This discovery has particular utility where spent gas is upgraded in a catalytic reformer by reacting the CO and H 0 in the spent gas with a hydrocarbon to form H and CO. Thepresence of .the'H S in aspent gas neutralizes the effect'of the catalyst resulting in a reaction which is reduced considerably. In utilizing this discovery, a more advantageous method and means for metallizing iron oxides has been found which results in more production even'where the need to eliminate sulphur does not exist.

In the single figure of the drawing, a cross sectional view, partially schematic, of an apparatus is shown which utilizes and demonstrates the invention of this disclosure.

Referring to the drawing, a vertical shaft type reduction furnace is shown generally at 10, having a feed hopper 12 into which iron oxide pellets, compacts, or lumps 14 are fed. The pellets l4 descendby gravity into the shaft furnace from hopper 12 through a pellet feed pipe 16. The pellet feed pipe 16 also serves as a the discharge pipe 18 and receives metallic iron pellets,

hereinafter referred to as metallized pellets, thereby establishing gravitational descent of the pellet burden in shaft furnace 10.

At the upper portion of shaft furnace 10 is a bustle and tuyere system, indicated generally at 22, through which hot reducing gas at a temperature between 1,250 and l,500 F. is introduced to flow upwardly in a pellet reduction region 23 in counterflow relationship to the pellets 14, as shown by the arrows, and exits from the furnace through a gas off-take pipe 24 located at the top of the furnace. The pellet feed pipe 16 extends below the off-take pipe 24, which geometric arrangement creates a spent gas disengaging plenum 26 that permits spent gas to disengage from the pellet stockline and flow freely to the off-take pipe. The hot reducing gas, in flowing from bustle and tuyere system 22 of offtake pipe 24, serves to heat the iron oxide pellets and to reduce them to metallic iron.

The spent gas from off-take pipe 24 flows through a pipe 28 to a cooler-scrubber 30 which is provided to cool the spent gas and remove dust.-Cooler-scrubber 30 can be of any conventional type such as, for example, a packed tower with the gas flowing upward through the packing counterflow to cooling water. Cooled spent gas is introduced to a lower region of shaft furnace 10 through a cooling inlet pipe 32 which connects to a cooling gas introduction and distributing member 34 located within the furnace and arranged to distribute the cooled spent gas into the pellet burden. A blower 36 together-with a flow regulating valve 38 serves to admit the cooled spent gas. The cooled spent gas introduced into the burden at distributing member 34 flows upward in a pellet cooling region 39 in counterflow relationship to the descending pellets and disengages from the burden at a cooling region off-take member 40 which connects to a cooling region off-take pipe 42. The spent gas from off-take pipe 42 flows through a pipe 44 to a cooler-scrubber 46 which is provided to cool and scrub dust out of the spent gas which has passed through pellet cooling region 39 of the shaft furnace l0.

A reformer furnace 48 having fuel fired burners 50,

a flue pipe 52, and a plurality of catalytic reformer tubes 54, only one being shown, is utilized to generate hot reducing gas. Combustion air from a blower 56 is fed toburners 50 through a flow regulating valve 58. Fuel is fed to burners 50 through pipe 60 from a fuel source 64 and flow regulating valve 66.

A temperature sensing element 74 serves to control the burners 50 to maintain the temperature above 1,600 F normally in the range of l,600 to 2,000 F., in the reformer furnace 48 by control of flow regulating valve 58 in conventional fashion. The proper air to fuel ratio for burners 50 is maintained by conventional means, not shown, which serves to-regulate flow regulating valve 66.'Although the reformerfurnace 48 arrangement herein described is a preferred embodiment, other arrangements of reformer furnace might be employed.

Hydrocarbon from a source 76 is admitted to a mixer 80 through a flow regulating valve 78. Spent gas from cooler-scrubber 46 is admitted to mixer 80 by a blower 82 through a flow regulating valve 84. The hydrocarbon/spent gas mixture from mixer 80 is introduced to reformer tubes 54. through pipe 86. Hot reformed gas from reformer tubes 54, which gas serves as the reducing gas for shaft furnace 10, is fed to a gas inlet pipe 88 through apipe 90, a gas cooler 92, and a pipe 94. Another pipe 95 maybe connected to pipe 94 for addition of another gas to the system, such as'a hydrocarbon,.

CH CO A 2C0 2H CH H O A CO 3H The volume gain due to reforming is vented as off-gas by a suitable vent pipe 70 adjacent cooler-scrubber 30.

If desired, the off-gas from vent pipe 70 can be utilized as supplemental fuel for the reformer furnace to reduce the fuel required from fuel source 64.

Hot reformed gas which is suitable for use as a reducing gas for the direct reduction of iron oxide to metallic iron will contain a relatively high percentage of reductants CO and H A high quality hot reducing gas made by reforming a gaseous hydrocarbon such as natural gas, utilizing CO and residual water vapor in spent gas from a direct reduction furnace as the reforming oxidants, will contain at least 40 percent to 50 percent H lt has been found by experience thata hot reducing gas containing such amount of H will react with residual sulphur compounds in iron oxide pellets to form H S gas (hydrogen sulphide) which leaves the reduction furnace in the spent gas. In the reforming of natural gas with the spent gas from a direct reduction furnace, it has been found that H S in the spent gas in amounts of only to parts per million has an extremely adverse effect on the reformingcapacity of a reformer- It has further been found .that freshly mademetallized pellets, which are a highly porous form of sponge iron, will remove H 8 from spent gas, probably by the reaction of metallic iron with H S to form an iron sulphide. The freshly made metallized pellets will remove the H 8 at ambient temperature of 60 to 70 F., as well as at elevated temperatures.

In the present invention, the spent gas from the shaft type reduction furnace 10 is cooled in cooler-scrubber 30 wherein most of the water vapor formed during the reduction of the iron oxide pellets in the reduction region 23 is condensed. This condensing of water vapor upgrades the CO and H content of the spent gas and makes it a suitable gas for cooling the metallized pellets in the cooling region 39, without encountering reoxida tion of the pellets. The upgraded spentgas which is introduced into the furnace through distributing member 34 serves to cool the metallized pellets under reducing conditions, while the freshly metallized pellets descending in the cooling region 39 serve to remove any H S from the spent gas prior to its leaving the. furnace through offtake pipe '42. Thus, any residual sulphur which is removed from the iron oxide pellets in the upper part of the reduction region 23, before the oxide pellets are reduced to metallic iron, is put back into the metallized pellets in the cooling region 13, thereby providing sulphur-free off-gas for the reformer.

'ln'the operation of the overall process depicted schematically in drawing, the flow of the spent gas through valve 38 is adjusted to substantially match the flow of spent gas through valve 84 to avoid interchange of gases between the reduction region 23 and the cooling region 39 of the shaft furnace 10. Under some circumstances, it may be desirable to adjust the flow through valve 84 to be somewhat greater than that through valve 38to divert a portion of the reducing gas toward the cooling zone 39 and provide an added increment of reduction time of the pellets prior to their being cooled. In addition, a small amount of a hydrocarbon, such. as natural gas or methane, may be added to the reducing gas through pipe 95. The hydrocarbon will react in the reduction region 23 with the iron oxides to produce H and- CO, and that portion directed toward the cooling zone will pyrolyze to form carbon and hydrogen. The presence of the additional carbon is useful during the subsequent melting of the metallized pellets, and the hydrogen is obviously beneficial. It has been found that the amount of hydrocarbon should not exceed 6 percent of the amount of gas in pipe 94; otherwise, carbon deposits would be excessive.

.An alternate embodiment includes a sulphur removal unit '72 having a bed of active iron particles 73. As the spent gas leaves the scrubber-cooler 30, it passes into the sulphur removal unit 72 and the gases come in contact with the activated iron particles 73. After the gas is exposed to the particles 73, it then passes into the cooling inlet pipe 32 where it serves to cool the pellet burden. This particular embodiment is useful where the quantity of sulphur in the original iron ore is too high for acceptance, or there is a desire to produce substantially sulphur free iron. The activated pellets 73 placed into the bed 72 would serve as scavenger pellets and would remove virtually all of the sulphur in the spent gas. With such removal, the gas going back into the cooling pipe 32 would lack the presence of sulphur, thereby eliminating its deposit in the final product. Although the scavenger metallized pellets 73 would have to be changed periodically, it has been found that the activity of the iron with respect to sulphur removal is extremely high, and the percentage of scavenger pellets to final product is small. The sulphur removal unit 72 may be placed, alternately, intermediate the off-take pipe 24 and scrubber-cooler 30.

In order to gain an insight into the ability of activated iron particles to extract sulphur from a gas stream containing hydrogen, a test was conducted. Activated pellets wereemployedwhich had the following analysis:

Total lron Metallic lron Metallized Carbon Sulphur The pellet sample was placed in a Burrell tube furnace with a control thermocouple within the bed. This couple was maintained at F. throughout the test. 5 CFH of an endothermic generated gas (approximately 20 percent CO, 40 percent H and 38 percent N to which was added 5 percent bott1ed H S, was passed through the pellet bed. Several pellets were re- Time Sulphur in Bed 1 Hour 0.14 2 Hours 0.17 3 Hours 0.23 6 Hours 0.39 l2 Hours 1.82 24 Hours 2.67 36 Hours 2.80

These tests confirm that activated iron particles have the ability to absorb sulphur from an H 8 bearing gas over a long period.

Although only a few embodiments have been shown and described, modification therein and other embodiments will be readily apparent to those skilled in the art, and no limitation in the scope of the invention is intended except as limited by the following claims.

I claim:

1. In a method for metallizing iron oxide particles which contain sulphur in a form that will react with a reductant to produce a gas containing a sulphur compound, the steps comprising: supplying particles to the upper portion of a vertically aligned shaft furnace, re moving said particles from the'bottom of said shaft furnace to produce a gravitationally descending bed of particles, supplying to the furnace a hot reducing gas, between 1,250 and 1,500 E, which comprises H and CO, thereby reducing the iron oxide and producing a spent gas containing H and CO removing the spent gas near the top of the shaft furnace, cooling the spent gas after it exits from the furnace, supplying the cooled spent gas to the bottom of the shaft furnace, removing the spent gas from a location intermediate the bottom and the place where the reducing gas is originally supplied to the shaft furnace, mixing the gas with a hydrocarbon, supplying the mixed gas to a catalytic reforming furnace, heating the reforming furnace to react the spent gas and hydrocarbon to form CO and H and directing the reformed gas from the reforming furnace to the vertical shaft furnace.

2. In a method for metallizing iron oxides in a gaseous reduction process wherein the spent gas is reformed to produce a reducing gas, the steps comprising: feeding a supply of oxide particles to the upper portion of a vertically aligned furnace, removing the particles from the bottom of the furnace thereby causing a gravitational flow of particles within the furnace, supplying a hot reducing gas to an intermediate part of the furnace, removing spent gas at the upper portion of the furnace, cooling the spent gas after it is withdrawn from the furnace, directing the thusly cooled gas to the bottom portion of the furnace, removing the cooled gas from the furnace intermediate the location where the hot reducing gas is supplied and the bottom portion of the furnace, mixing the thusly removed gas with a hydrocarbon, directing the mixture toa reforming furnace, heating the reforming furnace about 1,600 F and directing the products from the reforming furnace to the intermediate part of the shaft furnace.

3. The method of claim 2 including the step of adding up to 6 percent hydrocarbon to the reducing gas after it leaves the reformer.

UNITED STATES PATENT AND TRADEMARK OFFICE CERTIFICATE OF CORRECTION PATENT NO. 3,816,101

DATED 1 June 11, 197

INVENTOR(S) Donald Beggs and M I I iam T. Marston It is certified that error appears in the above-identified patent and that said Letters Patent are hereby corrected as shown below:

Column 1, line 35, change wherefull" to where full Column 6, line 28, change about to above Signed and Scaled this eleventh Day of May 1976 [SEAL] Altesl.

RUTH C. MASON C. MARSHALL DANN Arresting ()jfice'r ('nmmissimu'r nj'lau'nls and Trademarks 

2. In a method for metallizing iron oxides in a gaseous reduction process wherein the spent gas is reformed to produce a reducing gas, the steps comprising: feeding a supply of oxide particles to the upper portion of a vertically aligned furnace, removing the particles from the bottom of the furnace thereby causing a gravitational flow of particles within the furnace, supplying a hot reducing gas to an intermediate part of the furnace, removing spent gas at the upper portion of the furnace, cooling the spent gas after it is withdrawn from the furnace, directing the thusly cooled gas to the bottom portion of the furnace, removing the cooled gas from the furnace intermediate the location where the hot reducing gas is supplied and the bottom portion of the furnace, mixing the thusly removed gas with a hydrocarbon, directing the mixture to a reforming furnace, heating the reforming furnace about 1,600* F., and directing the products from the reforming furnace to the intermediate part of the shaft furnace.
 3. The method of claim 2 including the step of adding up to 6 percent hydrocarbon to the reducing gas after it leaves the reformer. 